Nickel-based alloy ndi mtundu wapadera wa aloyi womwe umakhala ndi faifi tambala, pomwe doping pang'ono zinthu zina, monga chitsulo, chromium, manganese ndi zina zotero.Alloy iyi imakhala ndi kukana kwa dzimbiri komanso kulimba kwa kutentha kwambiri.Nickel-based alloy powder ndi ufa wabwino kwambiri wopangidwa ndi tinthu tating'ono ta nickel-based alloy particles.Poyerekeza ndi ufa wachitsulo wachikhalidwe, ufa wa nickel-based alloy uli ndi kukana kwa dzimbiri komanso kutentha kwambiri.Panthawi yopangira, tinthu tating'onoting'ono timasungunuka bwino ndikuyika pansi kuti zitsimikizire kuti ali ndi thupi komanso mankhwala.Nickel-based alloy powder ali ndi ntchito zambiri ndipo angagwiritsidwe ntchito popanga zida zogwira ntchito kwambiri komanso zomangamanga.
Kanthu | Zamakono | Yendani | Kuchulukana | Kuuma | Kukula | Zamkatimu | Mapulogalamu |
HRNi20A | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 18-22 HRC | -106+45um -90+45um | C:0.1 Kr:4.5 Ndi: 2.0 B:0.7 Ndi: bala. | Kupopera kwamoto / kusakaniza, nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
HRNi22A | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 20-24 HRC | -106+45um -90+45um | C:0.2 Kr:1.0 Ndi:2.8 B:1.4 Fe: 1.0 Mn:0.1 Ndi: bala. | Kupopera kwamoto/kuphatikiza nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
HRNi25 | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 22-27HRC | -106+45um -90+45um | C:0.2 Kr:1.0 Ndi:3.5 B:1.5 Fe:8.0 Ndi: bala. | Kupopera kwamoto/kuphatikiza nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
HRNi28A | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 26-30 HRC | -106+45um -90+45um | C:0.1 Kr:3.0 Ndi:2.6 B:1.0 Ndi: bala. | Kupopera kwamoto/kuphatikiza nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
Mtengo wa HRNi35 | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 32-37HRC | -106+45um -90+45um | C: 0.3 Kr:10 Ndi:3.5 Fe:10 B:2.0 Ndi: bala. | Kupopera kwamoto/kuphatikiza nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
HRNi37A | Gasi Atomized | 12-17s / 50g | 3.5-4.5g/cm3 | 35-40HRC | -106+45um -90+45um | C:0.15 Kr:4.5 Ndi:2.6 B:1.2 Ndi: bala. | Kupopera kwamoto/kuphatikiza nkhungu yagalasi, kuponyera kosiyanasiyana kumafa. |
Mtengo wa HRNi45A | Madzi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 42-47HRC | -106+45um -90+45um | C:0.4 Si:3 B:2.6 Kr:12 Fe:5 Ndi: bala. | Flame spray / fusing HVOF, Seal pamwamba, nkhonya, vavu, pisitoni etc. |
Mtengo wa HRNi50A | Madzi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 45-50HRC | -106+45um -90+45um | C: 0.5 Ndi:3.0 B:3.0 Kr:12 Fe:5 Ndi: bala. | Flame spray/fusing HVOF, Seal surface, mafuta plunger ndi shaft etc. |
Mtengo wa HRNi55A | Madzi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 52-55HRC | -106+45um -90+45um | C: 0.8 Ndi:4.0 B:3.0 Kr:14 Fe: 5.0 Ndi: bala. | Flame spray/fusingHVOF, Seal pamwamba, mafuta plunger ndi kutsinde etc. |
Mtengo wa HRNi60A | Madzi atomized Gasi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um | C: 0.9 Ndi:4.0 B:3.2 Kd:16 Fe: 5.0 Ndi: bala. | Kupopera kwamoto / kusakaniza HVOF, kukana kwa dzimbiri bwino, kuuma kwambiri, kuvala bwino kumakana magwiridwe antchito, kutsika kwamphamvu kwamphamvu. |
Mtengo wa HRNi60CuMo | Madzi atomized Gasi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um | C: 0.9 Ndi:4.0 B:4.0 Kd:16 ku:3.0 Mo:3.0 Fe: 5.0 Ndi: bala. | Flame spray/fusing HVOF, fix, impeller, piston, valve etc. |
Mtengo wa HRNi65A | Madzi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 60-65HRC | -106+45um -90+45um | C:1.1 Ndi:4.0 B:4.0 Kd:18 Fe: 5.0 Ndi: bala. | Flame spray/fusingHVOF, kuuma kwambiri kuposa Ni60A, waya wodzigudubuza, plunger, conveyor roller etc. |
Mtengo wa HRNI625 | Madzi atomized Gasi atomized | 17-21s / 50g | 3.5-4.5g/cm3 | 8-15HRC | -106+45um -90+45um -45+15um | C:0.1 Ndi: 0.5 B:0.5 Kd:21 Mo:8.5 Nd:4.0 Fe: 5.0 Mn: 0.5 Ndi: bala. | Flame spray/fusing HVOF, kupuma kwa dzimbiri komanso anti-high heat oxided performance, |
PS: Timaperekanso ntchito zosinthidwa makonda |
1.Kuphimba wosanjikiza wapadera pazitsulo ndi zitsulo zigawo ndi magalasi ena amaumba kukonza.
2.Pre-chitetezo ndi kukonza kapena kulimbikitsa magawo amalonda.
3.Kwa FLS/PTA/APS/Laser Cladding application ndi kuphatikiza Ni kapena Nickel base alloy powder layers.
4.Kupanga zokutira zowirira kwambiri poyerekeza ndi FTC, komanso kuuma bwino komanso kufooka.